Summary of CO2 Welding Problems And Methods

Introduction:

In CO2 gas shielded welding, poor wire feeding and uneven wire output often occur during welding, which will bring difficulties to welding and directly affect welding quality. The weld that should be welded at a time is often divided into several sections to be welded. Based on my years of experience in welding operations, the author has summarized a set of elimination methods for the welding wire that is not unblocked during welding, which provides a solution for the problem of unblocked welding wire encountered when Changchun Rail Passenger Co., Ltd. produces welding Brazilian bogies when using new welding wires. Solution, the following experience is for reference only:

CO2 WELDING EFFECT

Nine reasons:
1 The welding wire has hard bends.
2 The welding wire is corroded.
3 The thickness of the welding wire is uneven.
4 Improper use of the wire feeder pinch roller.
5 The torch is too bent when used.
6 Grooves are ground in the welding gun wire feeding hose.
7 The contact tip has not been cleaned in time.
8 The wire feeding hole of the conductive nozzle is worn too much.
9 The current and voltage do not match during welding.
01, the welding wire has hard bends
Cause: The welding wire does not produce hard bends during production. This phenomenon occurs when the welding wire of the welding wire reel is scattered due to bumps during the transportation, or when the scattered welding wire is manually wound on the welding wire reel.

Caused phenomenon: After entering the wire feed wheel, the welding wire with hard bends will be blocked before entering the welding torch. , The contact tip will be burnt when the voltage is too high.

Note: When opening the package and installing the welding wire, carefully check the welding wire reel to confirm that the welding wire reel is intact and the welding wire is wound neatly before use. When handling the welding wire, be sure to handle it carefully to avoid knocking the welding wire reel and causing the welding wire to fall off. When rewinding the scattered welding wire to the welding wire reel, you should wrap it carefully with gloves to avoid hard bends.

02, the welding wire is corroded

Causes: damaged packaging during transportation of the welding wire, excessive moisture in the welding wire warehouse, excessive humidity, excessive storage time, and storage of the welding wire after being touched by hand.

Cause: During welding, when the corroded welding wire enters the wire feeder, the pinch roller will slip, which will affect the normal wire feeding. When the welding wire with rusty parts enters the welding gun, the diameter of the welding wire will increase, it will be blocked by the conductive tip and cannot be welded. If the current is too high, the conductive tip will be burned, the welding seam will be poorly formed, and there will be debris on the surface.

Note: When opening the welding wire package, check whether the welding wire is rusty. The rusty welding wire should be replaced in the welding wire library in time. The welding wire packaging must not be damaged. The humidity of the welding wire library should be controlled. The welding wire should be stored 300mm away from the ground and the wall, so that the welding wire purchased first is used first, and the welding wire used is rigorously touched by hand.
03, the welding wire has uneven thickness or burrs
Cause: It is caused by unqualified wire drawing equipment during the production of welding wire.

Cause: During welding, when welding wire with uneven thickness or burrs enters the welding gun wire feeding hose, it will friction with the hose wall and vibrate. When the vibration gradually approaches the welding gun and enters the conductive nozzle, the wire feeding will be unstable. , Intermittent welding or stuck phenomenon.

Note: Intermittent welding occurs after replacing the new contact tip. Use the contact tip of the matching model to check the welding wire before welding. It is found that the welding wire without the welding machine pinch wheel is not smooth when it passes through the contact tip of the matching model. The diameter of the welding wire must be uneven and the welding wire should be replaced.
04. Improper use of wire feeder pinch roller
Cause: The pinch wheel of the wire feeder should be matched with the welding wire when used. The solid carbon steel welding wire uses steel wheels, the flux-cored welding wire uses ceramic wheels, and the wheel groove model matches the wire diameter. The pressure should be adjusted according to the requirements of use, and should not be too loose or too tight.

Caused phenomenon: When the carbon steel solid core welding wire uses ceramic wheels, it will cause the ceramic wheels to wear too quickly. When a steel wire feed wheel is used for the flux-cored welding wire, the flux-cored wire will collapse and crack, causing the flux to leak out and be unable to weld.
When the diameter of the carbon steel solid welding wire is larger than the diameter of the wire feed wheel groove, it is easy to produce indentations on the welding wire, which will deform the circular section of the welding wire, and the welding wire with indentation will be stuck when passing through the contact tip.

When the diameter of the welding wire is smaller than the groove diameter of the wire feed wheel, the friction force between the wire feed wheel and the welding wire is insufficient and slips, and the wire cannot be fed normally.

When the diameter of the wire feed wheel and the welding wire match, the pressure of the wire feeder pinch wheel should also be appropriate.If the pressure of the wire feed wheel is too high, it will cause the welding wire to deform. , When the welding wire receives resistance in the wire feeding hose or on the contact tip, the wire feeding will be unstable.

Note: Use steel or ceramic wire feed wheels as required. The groove type of the wire feed wheel and the diameter of the welding wire must match the pressure of the wire feed wheel. The groove of the wire feed wheel must be cleaned frequently.
05. The torch is bent too much and too sharply when using it
Cause: Too random during welding or the special position of the welding seam makes the torch bend too much.

The phenomenon: it will cause the welding wire to be too blocked when running in the wire feeding hose of the welding gun, resulting in difficulty in wire out and unstable wire feeding.

Note: When welding, keep the welding torch as straight or bent as possible to reduce the running resistance of the welding wire in the wire feeding hose.
06. Grooves are ground in the welding gun wire feeding spring hose
Cause: The welding gun wire feeding spring hose has been used for too long, and the welding wire will grind out the groove inside the hose when the welding wire passes through the wire feeding hose.

Cause: When welding wire enters the groove ground in the wire feeding spring hose, when the torch moves and bends, it will cause the groove wire clamping phenomenon, which hinders the normal operation of the wire feeding.

Note: When the wire feeding spring hose is used for too long, the wire is not smooth, the wire feeding hose behind the torch handle trembles or the wire jam occurs with the change of the welding gun angle, the wire feeding spring hose should be replaced in time . Try to maintain a large bending angle of the welding gun to reduce the friction of the welding wire in the wire feeding hose. If the wire feeding spring hose is too short in the welding gun, the welding wire will bend inside the welding gun, resulting in poor wire feeding. When the wire feeding spring hose is too long inside the welding gun, it will bend, which will increase the friction resistance of the wire feeding and cause the wire feeding to be unstable.
07. The contact tip is not cleaned in time
Cause: When the welding specification is adjusted improperly, or the welding gun is too close to the molten pool, the welding spatter will stick to the contact tip. The longer the welding time, the more spatter will be spattered.

The phenomenon: the more splashes of the welding gun contact tip, the easier it is to block the wire hole of the contact tip, thereby increasing the resistance of wire feeding, causing the welding wire to be blocked or blocked.

Note: When welding, adjust the angle of the welding torch and the stretched length of the welding wire as required to reduce the generation of spatter, so that the spatter on the conductive tip is often cleaned up with needle-nose pliers, and the welding wire is extended out of the conductive tip 10~ 15cm long, use needle-nose pliers to bend the welding wire from the root of the contact tip and then quickly loosen it after rotating it clockwise or counterclockwise for 3 to 5 times. Use the power of the wire to grind the wire feeding hole of the contact tip.
08. Excessive wear of the wire feeding hole of the conductive nozzle
Cause: The contact tip after a long time of welding wire wear during welding will cause the wire feed hole to be too large.

Causing phenomenon: The conductive nozzle wire feed hole is too large to cause poor conductivity during welding, and the discharge of the welding wire and the conductive nozzle will make the wire feed unstable or stick to the conductive nozzle, accompanied by the phenomenon of the welding wire swinging back and forth in the molten pool, which affects the formation of the weld. .

Note: During welding, when it is found that the welding wire exits the contact tip and then swings back, and it is accompanied by adhesion to the contact tip, it should be replaced with a new contact tip in time. The contact tip of the welding gun should match the diameter of the welding wire. If the diameter of the contact tip hole is too small, the friction resistance will be too large and the welding wire will be blocked or blocked. The contact tip decisively will cause the welding wire to swing back and forth in the molten pool and make the weld poorly formed.
09. Voltage and current do not match during welding
Cause: Insufficient experience when adjusting and welding is not performed in accordance with the specified welding specifications.

Cause: When the current is too large and the voltage is too small, intermittent and unstable welding will occur, the welding spatter is too large, and the welding wire is excessively loud and chaotic in the molten pool. When the current is too small and the voltage is too large, the welding fume will be too large, the welding wire will be excessively low in the molten pool, and the welding wire and the conductive tip will melt and stick together at the same time, and welding will not be possible.

Note: According to the production needs, adjust according to the welding specification, so that the welding wire will melt in time when it enters the molten pool, and the sound of the welding wire will be uniform when it enters the molten pool.

Concluding remarks

In addition to the above nine reasons, there may also be poor quality of the welding machine, unstable operation of the wire feeding motor, inadequate bonding of the copper plating layer of the welding wire, copper powder drop, and clogging of the contact tip, which will lead to unstable wire feeding. If the fixed shaft of the wire feeder is too loose, it will cause the welding wire to loosen, and if it is too tight, it will cause excessive wire feeding resistance and unstable wire feeding. The looseness of the ground wire during welding or the rust in the contact area has not been cleaned up, resulting in excessive resistance and unstable arc, which will affect the wire feeding. If the contact tip is not tightened, the welding current and voltage will be unstable and the wire feeding will be unstable. A good welder can also judge the cause of uneven wire feeding based on the vibration of the welding wire running in the welding gun. During welding, when the jitter occurs behind the handle of the welding torch, most of the wire feeding hose is ground out of the groove; when the jitter moves forward with the wire, this phenomenon is mainly caused by bending or pressing on the welding wire. Marks and burrs; when chattering occurs in front of the torch handle, the contact tip should be replaced in time.

The above experience can provide judgment basis and solutions for the instability of wire feeding during CO2 gas shielded welding operation, thereby improving production and product quality


Post time: Aug-13-2021